Optical Distortion in Tempered or Toughened Glass


In my previous post on Glass Tempering or Toughening Process, I had mentioned how the process is executed and the physics involved (Refer Back). Also a brief mention how the toughened glass quality is assessed after it breaks, this is very important because safety is the reason for we spend on tempering. There are also other issues in terms of quality when glass is tempered. These are mainly optical distortion, roller marks, waviness and bend, edge strength, coating burns, fragmenting, burns, spontaneous breakage, etc.

High Optical Distortion

Quality of tempered glass mainly depends on the quality of equipments used and the quality control procedures adopted. Optical Distortion , is mainly a blurred appearance in images when seen through the glass, as well as on the reflection on the glass. This quality issue in tempered glass is common to all types of glasses. Even though minor levels of optical distortion is present in most of the tempered glasses, but it gets magnified when the quality is that poor and the glass is applied on high rise building facades. The minor level optical distortion is inherent on tempered glass, considering the fact that glass nearly reaches it’s softening point as it is heated up to a temperature of 726 degrees, and also the fact that this glass moves in rollers, therefore it is also called roller wave distortions. Such distortions could be easily identified in reflective and low-e coated glasses. Roller wave distortions could be easily controlled by adopting suitable technology and quality control procedures (use of forced convection furnaces instead of radiation furnaces).

Reflective glasses, as it’s name suggests, reflects heat incident on it. While tempering such glasses, the uncoated side of

Minimum Optical Distortion

the glass is in the bottom and the reflective side faces upwards, while inside the furnace. Since the coated side keeps on reflecting heat, the bottom side gets heated faster and wait for the top side to reach the same temperature. At this point, the bottom side is in contact with the rollers. This is the major factor for the cause of roller wave distortion in reflective glasses. Another cause for optical distortion is the difference in temperature across the furnace.

Optical distortion could be minimized to a great extend by following simple standards in terms of cleaning and maintaining the rollers and furnace, constant monitoring of temperature gradients inside the furnace and by immediately taking corrective action as and when such defects are observed.

Image Courtesy:

http://www.whereaboutsphoto.com/wp-content/uploads/2010/10/rosslin-003.jpg

http://www.lightingdesignlab.com/articles/glazing/fig%201sm.jpg

Advertisements

14 thoughts on “Optical Distortion in Tempered or Toughened Glass

    • Thank you for your comment. It would be more interesting if you could share how the optical distortion is measured and what kind of process you adopt to minimize it.

  1. Concerning the issue of tempered glass and distortion it can be solved by tempering the glass first, with no coating , and coated afterwards. This allows a much better control of the tempering, plus no damage to the coating is inflcited due to the heat process.

  2. Pingback: Your Questions About Tempered Glass Cost

  3. Pingback: Your Questions About Tempered Glass Code

  4. Pingback: Your Questions About Laminated Glass

  5. Pingback: Your Questions About Laminated Glass

  6. Pingback: Your Questions About Laminated Glass Windows

  7. Hi:
    Just wanted to point out that LiteSentry Corporation has been making commercial systems for online measurement of glass distortion from the tempering process. Their systems have been running at many sites around the world for almost 10 years. You can get more info at their website LiteSentry.com – Disclaimer I am associated with LiteSentry.

    • That sounds really interesting. Could you mail me the details on the systems that can measure glass distortion as an article with your company detials? I could enter the same as a post in the blog.

Leave a Reply

Fill in your details below or click an icon to log in:

WordPress.com Logo

You are commenting using your WordPress.com account. Log Out / Change )

Twitter picture

You are commenting using your Twitter account. Log Out / Change )

Facebook photo

You are commenting using your Facebook account. Log Out / Change )

Google+ photo

You are commenting using your Google+ account. Log Out / Change )

Connecting to %s